Jianping NIU
,
Kenu YANG
,
Tao JIN
,
Xiaofeng SUN
,
Hengrong GUAN
,
Zhuangqi HU
材料科学技术（英）
The variation of S content during VIM refining Ni-base superalloy using CaO crucible was studied. It was found that the desulphurization process could not be carried out by only using CaO crucible. The role of Al addition to desulphurization was also studied. Combining with the results of XRD and composition analysis of the CaO crucible, the mechanism of desulphurization was proposed. Thermodynamical calculation about the reaction between the interface of CaO crucible and liquid metal has been discussed. This work indicated that under proper refining technology the S content in the liquid Ni-base alloy could be reduced from 3×10-5 to 2×10-6-4×10-6.
关键词:
Ni-base superalloy
,
null
,
null
,
null
Wen LI
,
Tao JIN
,
Xiaofeng SUN
,
Yi GUO
,
Hengrong GUAN
,
Zhuangqi HU
材料科学技术（英）
The Ni-base single crystal superalloy was bonded by the transient liquid phase (TLP) bonding, using a Ni-base flexible metal cloth as an insert alloy. TLP bonding of superalloy was carried out at 1473~1523 K for 0.5~24 h in vacuum. The [001] orientation of each test specimen was aligned perpendicular to the joint interface. The bonded region was observed by optical microscopy, and the microstructural and compositional analyses across the bonded interlayer were performed by using a scanning electron microscopy (SEM). The electron back scattering diffraction (EBSD) method was applied to determine the crystallographic orientation. The results indicated that the chemical homogeneity across the bonded region can be achieved, and γ′ phase both in the bonded interlayer and in the superalloy substrate is almost identical, while the bonded interlayer had almost matched the crystallographic orientation of the bonded substrates.
关键词:
Single crystal superalloy
,
null
,
null
,
null